1. The amount of curing agent added should depend on the temperature, and decreases when the temperature is high. Excessive use of curing agents can cause the mold to become hard and brittle; If too little curing agent is used, the operation time will be prolonged. 2. To prevent changes in the physical properties of the mold silicone, it is recommended not to add silicone oil. 3. In order to achieve the best usage effect of your mold, please store the mold for at least 24 hours before use. 4. Hard molds can also be made of resin

1. Use a plastic bowl to hold 500g of adhesive, add 1.5% curing agent at room temperature, stir well and set aside. 2. Treat and lubricate the mother mold blank with a release agent. 3. The lubricated mother billet should be surrounded by wooden strips, which should also be treated with a release agent. The gap in the middle should be 2-4cm. 4. Slowly pour the prepared adhesive along a fixed pouring point and shake it from time to time to eliminate any air inside. 5. After 60 minutes of complete curing of the adhesive, wrap it around with wooden strips, leaving a 4cm gap, and fold off the original wooden strips. 6. Mix 1000g of gypsum powder with water and inject it into the wooden frame until it is full (the wooden frame should be divided into two parts using plastic sheets to facilitate mold removal). 7. After 20 minutes, remove the wooden strip and the mold will be completed.

① The cultural stone mold adhesive should have good operational performance. ② Silicone has better flowability and low viscosity, making it easy to operate. ③ The smaller the shrinkage rate of silicone rubber, the better. ④ Silicone rubber has better tensile strength. ⑤ The silicone mold made should not deform. ⑥ The hardness of silicone rubber should be suitable for product use. ⑦ High temperature resistance, multiple mold turns, longer service life, better, acid, alkali, and aging resistance.

Stir silicone and curing agent evenly. The appearance of the mold silicone is a flowing liquid, with component A being silicone and component B being curing agent. Example: Take 100 grams of silicone and add 2 grams of curing agent (note: silicone and curing agent must be stirred evenly. If not stirred evenly, one piece of the mold will have already solidified, and another piece will not have solidified. The silicone will have uneven drying and curing, which will affect the service life and number of mold turns of the silicone mold, and even cause the mold to be scrapped.

Thermal conductive potting adhesive, thermal conductive potting silicone, thermal conductive potting silicone rubber, thermal conductive potting silicone, and thermal conductive potting silicone are suitable for insulation and thermal potting of products such as electronics, power modules, high-frequency transformers, connectors, sensors, electric heating parts, and circuit boards.

1. This product is non-toxic and flame retardant, and is transported as a non hazardous material 2. Complies with UL-94-HB fire protection specifications 3. The packaging specifications are 5 kg/barrel and 20 kg/barrel 4. Typical technical indicators 5. Fully compliant with EU ROHS directive requirements

Encapsulated silicone, also known as two-component silicone additive thermal conductive encapsulation adhesive, belongs to silicone products. Synthetic rubber made from two different seasonings. characteristic

According to the weight, mix and stir evenly in a ratio of A: B=1:1 before applying the adhesive. Attention: In order to ensure the good performance of the product, components A and B need to be thoroughly mixed before 1:1 mixing. After each component is evenly mixed, they need to be weighed and sampled for proportioning. Then, the prepared adhesive should be evenly mixed before applying and sealing.

Heat conductive potting adhesive (HCY) is a low viscosity, flame retardant, two component addition molding silicone heat conductive potting adhesive that can cure at room temperature or heat, with the characteristic of faster curing at higher temperatures. It is a product made by ordinary sealing silicone or adhesive silicone with thermal conductivity added.